Microstructure and mechanical properties of the 2D C/SiC/TC4 joints brazed with Cu-Ti + Mo | |
Yang H. ; Fan S. ; Wang X. ; Cheng L. ; Zhang L. | |
2014 | |
会议名称 | 8th High Temperature Ceramic Matrix Composites Conference, HTCMC 2013, September 22, 2013 - September 26, 2013 |
会议地点 | Xi'an, Shaanxi, China |
页码 | 271-278 |
英文摘要 | Two-dimension carbon fiber reinforced silicon carbide ceramic matrix (2D C/SiC) composites were vacuum brazed to TC4 alloy using Cu-Ti + Mo composite filler. Effect of Mo content on the microstructure and mechanical properties of the joints were investigated. The results showed that joints were composed of four regions: a interface reaction layer, a stress relief layer, a residual Cu layer and a diffusion layer. With the increased Mo content, the flexural strength increased at first then decreased. The maximum flexural strength reached 130 MPa with 10 vol.% Mo particles in the filler. |
收录类别 | EI |
会议录 | 8th High Temperature Ceramic Matrix Composites Conference, HTCMC 2013, September 22, 2013 - September 26, 2013 |
会议录出版者 | American Ceramic Society |
会议录出版地 | Xi'an, Shaanxi, China |
语种 | 英语 |
内容类型 | 会议论文 |
源URL | [http://ir.ciomp.ac.cn/handle/181722/44563] |
专题 | 长春光学精密机械与物理研究所_中科院长春光机所知识产出_会议论文 |
推荐引用方式 GB/T 7714 | Yang H.,Fan S.,Wang X.,et al. Microstructure and mechanical properties of the 2D C/SiC/TC4 joints brazed with Cu-Ti + Mo[C]. 见:8th High Temperature Ceramic Matrix Composites Conference, HTCMC 2013, September 22, 2013 - September 26, 2013. Xi'an, Shaanxi, China. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论