Corrosion Resistance of Low Pressure Cold Sprayed Cu-Zn Composite Coatings | |
Feng, Li1,2; Chang, Jirong1; Li, Dongting1; An, Guosheng1,2; Li, Wensheng1,2 | |
刊名 | Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering |
2020-06-01 | |
卷号 | 49期号:6页码:2029-2038 |
关键词 | Binary alloys Chlorine compounds Chromate coatings Chromium plating Composite coatings Copper oxides Corrosion resistance Corrosion resistant coatings Electrochemical corrosion Oxide minerals Sprayed coatings Zinc coatings Chrome plating Coated sample Cold spray techniques Copper and zinc Corrosion performance Corrosion products Corrosion tests Low pressures |
ISSN号 | 1002185X |
英文摘要 | Copper-zinc coated samples were prepared by a low-pressure cold spray technique on 45# steel substrate and 45# steel plus chrome-plated substrate. Corrosion performance of coatings and coatings plus chrome plating layer was investigated by static soaking and copper accelerated acetate spray corrosion test (CASS). The microstructure and elements valence stage of the coating and chrome plating layer before and after corrosion were characterized by SEM and XPS. The results show that the corrosion resistance of copper-zinc coating is better than that of copper-zinc coating plus chrome plating layer during static corrosion. In the CASS test, with the increase of zinc content in the original powder, the corrosion resistance of the coating sample and the coating plus chrome plating sample is improved. When the copper-zinc ratio is 6:4, the corrosion resistance of the corresponding coating sample, the coating plus chrome layer sample and the pure chrome layer reaches the sixth grade. Copper and zinc coatings are corroded in the corrosive liquid due to electrochemical corrosion and chlorination. The corrosion products are mainly Zn(OH)2, Cu2O and CuCl2. In the process of corrosion of copper-zinc coating plus chrome-plated layer samples, the corrosion of zinc can play a role in slowing the corrosion of chrome plating. The effect of the mitigation together with the copper film deposited on the chrome-plated layer protects the chrome-plated layer and enhances its corrosion resistance. © 2020, Science Press. All right reserved. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 中文 |
出版者 | Rare Metals Materials and Engineering Press |
WOS记录号 | WOS:000552452000029 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/115477] |
专题 | 材料科学与工程学院 |
作者单位 | 1.School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou; 730050, China; 2.State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou; 730050, China |
推荐引用方式 GB/T 7714 | Feng, Li,Chang, Jirong,Li, Dongting,et al. Corrosion Resistance of Low Pressure Cold Sprayed Cu-Zn Composite Coatings[J]. Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering,2020,49(6):2029-2038. |
APA | Feng, Li,Chang, Jirong,Li, Dongting,An, Guosheng,&Li, Wensheng.(2020).Corrosion Resistance of Low Pressure Cold Sprayed Cu-Zn Composite Coatings.Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering,49(6),2029-2038. |
MLA | Feng, Li,et al."Corrosion Resistance of Low Pressure Cold Sprayed Cu-Zn Composite Coatings".Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering 49.6(2020):2029-2038. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论