Experimental study on very high cycle fatigue of martensitic steel of 2Cr13 under corrosive environment | |
Li, S. X.; Zhang, P. Y.; Yu, S. R. | |
刊名 | FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES |
2014-10 | |
卷号 | 37期号:10页码:1146-1152 |
关键词 | crack initiation fatigue limit S-N curve very high cycle fatigue |
ISSN号 | 8756-758X |
DOI | 10.1111/ffe.12197 |
英文摘要 | Rotating bending fatigue test at very high cycle regimes was carried out on martensitic steel of 2Cr13 in air and 3.5% NaCl environment. The result showed that the S-N curve presents a stepwise tendency over the range of 10(6)-10(8) cycles in both air and 3.5% NaCl environment. In air fatigue, cracks initiated from the sample surface and inclusions at subsurface and no typical fish eye feature in very high cycle fatigue were observed for all samples tested up to 6 x 108 cycles. In 3.5% NaCl solution, a fatigue limit over the range of 10(6)-10(8) cycles exhibited with the corrosion fatigue strength reduced by 47% compared to the air fatigue. Multiple cracks initiated from surface and the number of crack origins increased with increasing stress level and surface proportion of fatigue propagation increased as number of cycles increased. |
资助项目 | National Science Foundation of China[51275225] ; Hongliu Excellence Youth Plan of Lanzhou University of Technology[J201302] |
WOS研究方向 | Engineering ; Materials Science |
语种 | 英语 |
出版者 | WILEY-BLACKWELL |
WOS记录号 | WOS:000341195000008 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/34270] |
专题 | 兰州理工大学 |
通讯作者 | Li, S. X. |
作者单位 | Lanzhou Univ Technol, Sch PetroChem Engn, Lanzhou 730050, Peoples R China |
推荐引用方式 GB/T 7714 | Li, S. X.,Zhang, P. Y.,Yu, S. R.. Experimental study on very high cycle fatigue of martensitic steel of 2Cr13 under corrosive environment[J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES,2014,37(10):1146-1152. |
APA | Li, S. X.,Zhang, P. Y.,&Yu, S. R..(2014).Experimental study on very high cycle fatigue of martensitic steel of 2Cr13 under corrosive environment.FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES,37(10),1146-1152. |
MLA | Li, S. X.,et al."Experimental study on very high cycle fatigue of martensitic steel of 2Cr13 under corrosive environment".FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES 37.10(2014):1146-1152. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论