Corrosion Mechanism of E-glass of Chemical Resistance Glass Fiber in Acid Environment | |
Xie, Jun; Yin, Peng; Shi, Weiguang; Hu, Min; Wang, Jing; Zhou, Xuedong; Han, Jianjun; Cao, Shaowen; Han, Lixiong; Yao, Yuan | |
刊名 | Journal Wuhan University of Technology, Materials Science Edition |
2016 | |
卷号 | 31期号:4页码:872-876 |
关键词 | ECR hinder destroyed sizing adhere totally boron melting reaches leaching inorganic |
ISSN号 | 1000-2413 |
DOI | 10.1007/s11595-016-1461-1 |
URL标识 | 查看原文 |
WOS记录号 | WOS:000385034600027;EI:20163102671716 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/3388783 |
专题 | 武汉理工大学 |
作者单位 | 1.[Hu, Min 2.Yin, Peng 3.Shi, Weiguang 4.Cao, Shaowen 5.Xie, Jun 6.Zhou, Xuedong 7.Han, Jianjun 8.Wang, Jing] Wuhan Univ Technol, State Key Lab Silicate Mat Architectures, Wuhan 430070, Peoples R China. |
推荐引用方式 GB/T 7714 | Xie, Jun,Yin, Peng,Shi, Weiguang,et al. Corrosion Mechanism of E-glass of Chemical Resistance Glass Fiber in Acid Environment[J]. Journal Wuhan University of Technology, Materials Science Edition,2016,31(4):872-876. |
APA | Xie, Jun.,Yin, Peng.,Shi, Weiguang.,Hu, Min.,Wang, Jing.,...&Yao, Yuan.(2016).Corrosion Mechanism of E-glass of Chemical Resistance Glass Fiber in Acid Environment.Journal Wuhan University of Technology, Materials Science Edition,31(4),872-876. |
MLA | Xie, Jun,et al."Corrosion Mechanism of E-glass of Chemical Resistance Glass Fiber in Acid Environment".Journal Wuhan University of Technology, Materials Science Edition 31.4(2016):872-876. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论